Polymer binder for lithium battery and method of manufacturing

ABSTRACT

Provided is an anode active material layer for a lithium battery. The anode active material layer comprises multiple anode active material particles and an optional conductive additive that are bonded together by a binder comprising a high-elasticity polymer having a recoverable or elastic tensile strain no less than 10% when measured without an additive or reinforcement in the polymer and a lithium ion conductivity no less than 10 −5  S/cm at room temperature. The anode active material preferably has a specific lithium storage capacity greater than 372 mAh/g (e.g. Si, Ge, Sn, SnO 2 , Co 3 O 4 , etc.).

FIELD OF THE INVENTION

The present invention relates generally to the field of rechargeable lithium battery and, more particularly, to the lithium battery anode and cell, and the method of manufacturing same.

BACKGROUND OF THE INVENTION

A unit cell or building block of a lithium-ion battery is typically composed of an anode current collector, an anode or negative electrode layer (containing an anode active material responsible for storing lithium therein, a conductive additive, and a resin binder), an electrolyte and porous separator, a cathode or positive electrode layer (containing a cathode active material responsible for storing lithium therein, a conductive additive, and a resin binder), and a separate cathode current collector. The electrolyte is in ionic contact with both the anode active material and the cathode active material. A porous separator is not required if the electrolyte is a solid-state electrolyte.

The binder in the anode layer is used to bond the anode active material (e.g. graphite or Si particles) and a conductive filler (e.g. carbon black particles or carbon nanotube) together to form an anode layer of structural integrity, and to bond the anode layer to a separate anode current collector, which acts to collect electrons from the anode active material when the battery is discharged. In other words, in the negative electrode (anode) side of the battery, there are typically four different materials involved: an anode active material, a conductive additive, a resin binder (e.g. polyvinylidine fluoride, PVDF, or styrene-butadiene rubber, SBR), and an anode current collector (typically a sheet of Cu foil).Typically the former three materials form a separate, discrete anode active material layer (or, simply, anode layer) and the latter one forms another discrete layer.

A binder resin (e.g. PVDF or PTFE) is also used in the cathode to bond cathode active materials and conductive additive particles together to form a cathode active layer of structural integrity. The same resin binder also acts to bond this cathode active layer to a cathode current collector.

The most commonly used anode active materials for lithium-ion batteries are natural graphite and synthetic graphite (or artificial graphite) that can be intercalated with lithium and the resulting graphite intercalation compound (GIC) may be expressed as Li_(x)C₆, where x is typically less than 1. The maximum amount of lithium that can be reversibly intercalated into the interstices between graphene planes of a perfect graphite crystal corresponds to x=1, defining a theoretical specific capacity of 372 mAh/g.

Graphite or carbon anodes can have a long cycle life due to the presence of a protective solid-electrolyte interface layer (SEI), which results from the reaction between lithium and the electrolyte (or between lithium and the anode surface/edge atoms or functional groups) during the first several charge-discharge cycles. The lithium in this reaction comes from some of the lithium ions originally intended for the charge transfer purpose. As the SEI is formed, the lithium ions become part of the inert SEI layer and become irreversible, i.e. these positive ions can no longer be shuttled back and forth between the anode and the cathode during charges/discharges. Therefore, it is desirable to use a minimum amount of lithium for the formation of an effective SEI layer. In addition to SEI formation, the irreversible capacity loss Q_(ir) can also be attributed to graphite exfoliation caused by electrolyte/solvent co-intercalation and other side reactions.

In addition to carbon- or graphite-based anode materials, other inorganic materials that have been evaluated for potential anode applications include metal oxides, metal nitrides, metal sulfides, and the like, and a range of metals, metal alloys, and intermetallic compounds that can accommodate lithium atoms/ions or react with lithium. Among these materials, lithium alloys having a composition formula of Li_(a)A (A is a metal or semiconductor element, such as Al and Si, and “a” satisfies 0<a≤5) are of great interest due to their high theoretical capacity, e.g., Li₄Si (3,829 mAh/g), Li_(4.4)Si (4,200 mAh/g), Li_(4.4)Ge (1,623 mAh/g), Li_(4.4)Sn (993 mAh/g), Li₃Cd (715 mAh/g), Li₃Sb (660 mAh/g), Li_(4.4)Pb (569 mAh/g), LiZn (410 mAh/g), and Li₃Bi (385 mAh/g). However, as schematically illustrated in FIG. 2, in an anode composed of these high-capacity anode active materials, severe pulverization (fragmentation of the alloy particles) and detachment of active material particles from the resin binder occur during the charge and discharge cycles. These are due to severe expansion and contraction of the anode active material particles induced by the insertion and extraction of the lithium ions in and out of these particles. The expansion and contraction, the resulting pulverization, of active material particles and detachment from the resin binder lead to loss of contacts between active material particles and conductive additives and loss of contacts between the anode active material and its current collector. These adverse effects result in a significantly shortened charge-discharge cycle life.

To overcome some of the problems associated with such mechanical degradation, three technical approaches have been proposed:

-   (1) reducing the size of the active material particle, presumably     for the purpose of reducing the total strain energy that can be     stored in a particle, which is a driving force for crack formation     in the particle. However, a reduced particle size implies a higher     surface area available for potentially reacting with the liquid     electrolyte to form a higher amount of SEI. Such a reaction is     undesirable since it is a source of irreversible capacity loss. -   (2) depositing the electrode active material in a thin film form     directly onto a current collector, such as a copper foil. However,     such a thin film structure with an extremely small     thickness-direction dimension (typically much smaller than 500 nm,     often necessarily thinner than 100 nm) implies that only a small     amount of active material can be incorporated in an electrode (given     the same electrode or current collector surface area), providing a     low total lithium storage capacity and low lithium storage capacity     per unit electrode surface area (even though the capacity per unit     mass can be large). Such a thin film must have a thickness less than     100 nm to be more resistant to cycling-induced cracking, further     diminishing the total lithium storage capacity and the lithium     storage capacity per unit electrode surface area. Such a thin-film     battery has very limited scope of application. A desirable and     typical electrode thickness is from 100 μm to 200 μm. These     thin-film electrodes (with a thickness of <500 nm or even <100 nm)     fall short of the required thickness by three (3) orders of     magnitude, not just by a factor of 3. -   (3) using a composite composed of small electrode active particles     protected by (dispersed in or encapsulated by) a less active or     non-active matrix, e.g., carbon-coated Si particles, sol gel     graphite-protected Si, metal oxide-coated Si or Sn, and     monomer-coated Sn nano particles. Presumably, the protective matrix     provides a cushioning effect for particle expansion or shrinkage,     and prevents the electrolyte from contacting and reacting with the     electrode active material. Examples of high-capacity anode active     particles are Si, Sn, and SnO₂. Unfortunately, when an active     material particle, such as Si particle, expands (e.g. up to a volume     expansion of 380%) during the battery charge step, the protective     coating is easily broken due to the mechanical weakness and/o     brittleness of the protective coating materials. There has been no     high-strength and high-toughness material available that is itself     also lithium ion conductive.

It may be further noted that the coating or matrix materials used to protect active particles (such as Si and Sn) are carbon, sol gel graphite, metal oxide, monomer, ceramic, and lithium oxide. These protective materials are all very brittle, weak (of low strength), and/or non-conducting (e.g., ceramic or oxide coating). Ideally, the protective material should meet the following requirements: (a) The coating or matrix material should be of high strength and stiffness so that it can help to refrain the electrode active material particles, when lithiated, from expanding to an excessive extent. (b) The protective material should also have high fracture toughness or high resistance to crack formation to avoid disintegration during repeated cycling. (c) The protective material must be inert (inactive) with respect to the electrolyte, but be a good lithium ion conductor. (d) The protective material must not provide any significant amount of defect sites that irreversibly trap lithium ions. (e) The protective material must be lithium ion-conducting as well as electron-conducting. The prior art protective materials all fall short of these requirements. Hence, it was not surprising to observe that the resulting anode typically shows a reversible specific capacity much lower than expected. In many cases, the first-cycle efficiency is extremely low (mostly lower than 80% and some even lower than 60%). Furthermore, in most cases, the electrode was not capable of operating for a large number of cycles. Additionally, most of these electrodes are not high-rate capable, exhibiting unacceptably low capacity at a high discharge rate.

Due to these and other reasons, most of prior art composite electrodes and electrode active materials have deficiencies in some ways, e.g., in most cases, less than satisfactory reversible capacity, poor cycling stability, high irreversible capacity, ineffectiveness in reducing the internal stress or strain during the lithium ion insertion and extraction steps, and other undesirable side effects.

Complex composite particles of particular interest are a mixture of separate Si and graphite particles dispersed in a carbon matrix; e.g. those prepared by Mao, et al. [“Carbon-coated Silicon Particle Powder as the Anode Material for Lithium Batteries and the Method of Making the Same,” US 2005/0136330 (Jun. 23, 2005)]. Also of interest are carbon matrix-containing complex nano Si (protected by oxide) and graphite particles dispersed therein, and carbon-coated Si particles distributed on a surface of graphite particles Again, these complex composite particles led to a low specific capacity or for up to a small number of cycles only. It appears that carbon by itself is relatively weak and brittle and the presence of micron-sized graphite particles does not improve the mechanical integrity of carbon since graphite particles are themselves relatively weak. Graphite was used in these cases presumably for the purpose of improving the electrical conductivity of the anode material. Furthermore, polymeric carbon, amorphous carbon, or pre-graphitic carbon may have too many lithium-trapping sites that irreversibly capture lithium during the first few cycles, resulting in excessive irreversibility.

In summary, the prior art has not demonstrated a composite material and other approaches that can effectively reduce or eliminate the expansion/shrinkage-induced problems of the anode active material in a lithium-ion battery. Thus, there is an urgent and continuing need for a new protective or binder material that enables a lithium-ion battery to exhibit a long cycle life. There is also a need for a method of readily or easily producing such a material in large quantities.

Thus, it is an object of the present invention to meet these needs and address the issues associated the rapid capacity decay of a lithium battery containing a high-capacity anode active material.

SUMMARY OF THE INVENTION

Herein reported is an anode active material layer for a lithium battery that contains a very unique class of binder resin. This binder resin contains a high-elasticity polymer that is capable of overcoming the rapid capacity decay problem commonly associated with a lithium-ion battery that features a high-capacity anode active material, such as Si, Sn, and SnO₂.

Specifically, the invention provides an anode active material layer for a lithium battery. This layer comprises multiple anode active material particles and an optional conductive additive (e.g. particles of carbon black, acetylene black, expanded graphite flakes, carbon nanotubes, graphene sheets, carbon nano-fibers, etc.) that are bonded together by a binder resin to form an anode active layer of structural integrity. This binder resin comprises a high-elasticity polymer having a recoverable tensile strain (elastic deformation) no less than 5% when measured without an additive or reinforcement in the polymer and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature.

The high-elasticity polymer has a recoverable tensile strain no less than 5% (typically 10-700%, more typically 30-500%, further more typically and desirably >50%, and most desirably >100%) when measured without an additive or reinforcement in the polymer under uniaxial tension. The polymer also has a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature (preferably and more typically no less than 10⁻⁴ S/cm and more preferably and typically no less than 10⁻³ S/cm). The anode active material preferably has a specific capacity of lithium storage greater than 372 mAh/g, which is the theoretical capacity of graphite.

High-elasticity polymer refers to a polymer, typically a lightly cross-linked polymer, which exhibits an elastic deformation that is at least 5% when measured (without an additive or reinforcement in the polymer) under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable upon release of the load and the recovery process is essentially instantaneous. The elastic deformation is preferably greater than 30%, more preferably greater than 50%, further more preferably greater than 100%, still more preferably greater than 150%, and most preferably greater than 200%.

In some preferred embodiments, the high-elasticity polymer contains a lightly cross-linked network of polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, ethylene oxide linkage, propylene oxide linkage, vinyl alcohol linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof, in the cross-linked network of polymer chains. These network or cross-linked polymers exhibit a unique combination of a high elasticity (high elastic deformation strain) and high lithium-ion conductivity.

In certain preferred embodiments, the high-elasticity polymer contains a lightly cross-linked network polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate (PETEA) chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.

In this anode active material layer, the anode active material may be selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo₂O₄; (f) prelithiated versions thereof; (g) particles of Li, Li alloy, or surface-stabilized Li having at least 60% by weight of lithium element therein; and (h) combinations thereof.

In some preferred embodiments, the anode active material contains a prelithiated Si, prelithiated Ge, prelithiated Sn, prelithiated SnO_(x), prelithiated SiO_(x), prelithiated iron oxide, prelithiated VO₂, prelithiated Co₃O₄, prelithiated Ni₃O₄, or a combination thereof, wherein x=1 to 2.

It may be noted that pre-lithiation of an anode active material means that this material has been pre-intercalated by or doped with lithium ions up to a weight fraction from 0.1% to 54.7% of Li in the lithiated product.

The anode active material is preferably in a form of nano particle (spherical, ellipsoidal, and irregular shape), nano wire, nano fiber, nano tube, nano sheet, nano belt, nano ribbon, nano disc, nano platelet, or nano horn having a thickness or diameter less than 100 nm. These shapes can be collectively referred to as “particles” unless otherwise specified or unless a specific type among the above species is desired. Further preferably, the anode active material has a dimension less than 50 nm, even more preferably less than 20 nm, and most preferably less than 10 nm.

In some embodiments, multiple particles are bonded by the high-elasticity polymer-based binder resin. A carbon layer may be deposited to embrace the anode active material particles prior to being bonded by the resin binder.

The anode active material layer may further contain a graphite, graphene, or carbon material mixed with the active material particles in the anode active material layer. The carbon or graphite material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, meso-phase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof. Graphene may be selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, hydrogenated graphene, nitrogenated graphene, functionalized graphene, etc.

The anode active material particles may be coated with or embraced by a conductive protective coating, selected from a carbon material, graphene, electronically conductive polymer, conductive metal oxide, or conductive metal coating. Preferably, the anode active material, in the form of a nano particle, nano wire, nano fiber, nano tube, nano sheet, nano belt, nano ribbon, nano disc, nano platelet, or nano horn is pre-intercalated or pre-doped with lithium ions to form a prelithiated anode active material having an amount of lithium from 0.1% to 54.7% by weight of said prelithiated anode active material.

Preferably and typically, the high-elasticity polymer has a lithium ion conductivity no less than 10⁻⁵ S/cm, more preferably no less than 10⁻⁴ S/cm, and most preferably no less than 10⁻³ S/cm. Some of the selected polymers exhibit a lithium-ion conductivity greater than 10⁻² S/cm. In some embodiments, the high-elasticity polymer is a neat polymer containing no additive or filler dispersed therein. In others, the high-elasticity polymer is a polymer matrix composite containing from 0.1% to 50% by weight (preferably from 1% to 35% by weight) of a lithium ion-conducting additive dispersed in a high-elasticity polymer matrix material. In some embodiments, the high-elasticity polymer contains from 0.1% by weight to 10% by weight of a reinforcement nano filament selected from carbon nanotube, carbon nano-fiber, graphene, or a combination thereof.

In some embodiments, the high-elasticity polymer is mixed with an elastomer selected from natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-E1), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.

In some embodiments, the high-elasticity polymer is a polymer matrix composite containing a lithium ion-conducting additive (0.1% to 50% by wt.) dispersed in a high-elasticity polymer matrix material, wherein the lithium ion-conducting additive is selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

In some embodiments, the high-elasticity polymer is a polymer matrix composite containing a lithium ion-conducting additive dispersed in a high-elasticity polymer matrix material, wherein the lithium ion-conducting additive contains a lithium salt selected from lithium perchlorate, LiClO₄, lithium hexafluorophosphate, LiPF₆, lithium borofluoride, LiBF₄, lithium hexafluoroarsenide, LiAsF₆, lithium trifluoro-metasulfonate, LiCF₃SO₃, bis-trifluoromethyl sulfonylimide lithium, LiN(CF₃SO₂)₂, lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium nitrate, LiNO₃, Li-Fluoroalkyl-Phosphates, LiPF₃(CF₂CF₃)₃, lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTF SI, an ionic liquid-based lithium salt, or a combination thereof.

The high-elasticity polymer may form a mixture or blend with an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.

In some embodiments, the high-elasticity polymer may form a mixture or blend with a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), Polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVdF), Poly bis-methoxy ethoxyethoxide-phosphazenex, Polyvinyl chloride, Polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, or a combination thereof. Sulfonation is herein found to impart improved lithium ion conductivity to a polymer.

The present invention also provides a lithium battery containing an optional anode current collector, the presently invented anode active material layer as described above, a cathode active material layer, an optional cathode current collector, an electrolyte in ionic contact with the anode active material layer and the cathode active material layer and an optional porous separator. The lithium battery may be a lithium-ion battery, lithium metal battery (containing lithium metal or lithium alloy as the main anode active material and containing no intercalation-based anode active material), lithium-sulfur battery, lithium-selenium battery, or lithium-air battery.

The present invention also provides a method of manufacturing a lithium battery. The method includes (a) providing a cathode active material layer and an optional cathode current collector to support the cathode active material layer; (b) providing an anode active material layer and an optional anode current collector to support the anode active material layer; and (c) providing an electrolyte in contact with the anode active material layer and the cathode active material layer and an optional separator electrically separating the anode and the cathode; wherein the operation of providing the anode active material layer includes bonding multiple particles of an anode active material and an optional conductive additive together to form the layer by a binder resin containing a high-elasticity polymer having a recoverable tensile strain from 5% to 700% when measured without an additive or reinforcement and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature.

Preferably, the high-elasticity polymer has a lithium ion conductivity from 1×10⁻⁵ S/cm to 2×10⁻² S/cm. In some embodiments, the high-elasticity polymer has a recoverable tensile strain from 10% to 300% (more preferably >50%, and most preferably >100%).

In certain preferred embodiments, the high-elasticity polymer contains a cross-linked network polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, ethylene oxide linkage, propylene oxide linkage, vinyl alcohol linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof in the cross-linked network of polymer chains.

Preferably, in the method, the high-elasticity polymer contains a cross-linked network of polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.

In certain embodiments, the binder resin contains a mixture/blend/composite of a high-elasticity polymer with an elastomer, an electronically conductive polymer (e.g. polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof), a lithium-ion conducting material, a reinforcement material (e.g. carbon nanotube, carbon nano-fiber, and/or graphene), or a combination thereof.

In this mixture/blend/composite, the lithium ion-conducting material is dispersed in the high-elasticity polymer and is preferably selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

In some embodiments, the lithium ion-conducting material is dispersed in the high-elasticity polymer and is selected from lithium perchlorate, LiClO₄, lithium hexafluoro-phosphate, LiPF₆, lithium borofluoride, LiBF₄, lithium hexafluoroarsenide, LiAsF₆, lithium trifluoro-metasulfonate, LiCF₃SO₃, bis-trifluoromethyl sulfonylimide lithium, LiN(CF₃SO₂)₂, lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium nitrate, LiNO₃, Li-Fluoroalkyl-Phosphates, LiPF₃(CF₂CF₃)₃, lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

In the invented method, the anode active material is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (c) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo₂O₄; (d) prelithiated versions thereof; (e) mixtures thereof with a carbon, graphene, or graphite material; (f) particles of Li, Li alloy, or surface-stabilized Li having at least 60% by weight of lithium element therein; and (f) combinations thereof.

Preferably, the anode active material particles are coated with a layer of carbon or graphene prior to being bonded by the high-elasticity polymer. Preferably, anode active material particles and particles of a carbon or graphite material are bonded together by the high-elasticity polymer. Preferably, the anode active material particles, possibly along with a carbon or graphite material and/or with some internal graphene sheets, are embraced by graphene sheets to form anode active material particulates, which are then bonded by the high-elasticity polymer. The graphene sheets may be selected from pristine graphene (e.g. that prepared by CVD or liquid phase exfoliation using direct ultrasonication), graphene oxide, reduced graphene oxide (RGO), graphene fluoride, doped graphene, functionalized graphene, etc.

The present invention also provides another method of manufacturing a lithium battery. The method comprises: (a) providing a cathode active material layer and an optional cathode current collector to support the cathode active material layer; (b) Providing an anode active material layer and an optional anode current collector to support the anode active material layer; and (c) providing an electrolyte in contact with the anode active material layer and the cathode active material layer and porous separator electrically separating the anode and the cathode; wherein the operation of providing the anode active material layer includes bonding multiple particles of an anode active material and an optional conductive additive together by a binder resin to form the anode active material layer and applying a thin film of a high-elasticity polymer to cover and protect the anode active material layer, wherein the high-elasticity polymer has a recoverable or elastic tensile strain from 5% to 700% when measured without an additive or reinforcement and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature and the thin film has a thickness from 1 nm to 10 μm. This thin film of high-elasticity polymer is implemented between the anode active material layer and the porous separator.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1(A) Schematic of a prior art lithium-ion battery cell, wherein the anode layer is a thin coating of an anode active material itself.

FIG. 1(B) Schematic of another prior art lithium-ion battery; the anode layer being composed of particles of an anode active material, a conductive additive (not shown) and a resin binder (not shown).

FIG. 2 Schematic illustrating the notion that expansion of Si particles, upon lithium intercalation during charging of a prior art lithium-ion battery, can lead to pulverization of Si particles, detachment of resin binder from the particles, and interruption of the conductive paths formed by the conductive additive, and loss of contact with the current collector;

FIG. 3(A) Representative tensile stress-strain curves of four BPO-initiated cross-linked ETPTA polymers.

FIG. 3(B) The specific capacity values of two lithium battery cells having an anode active material featuring (1) ETPTA polymer binder-bonded Co₃O₄ particles and SBR rubber-bonded Co₃O₄ particles.

FIG. 4(A) Representative tensile stress-strain curves of four PF5-initiated cross-linked PVA-CN polymers.

FIG. 4(B) The specific capacity values of two lithium battery cells having an anode active material featuring (1) high-elasticity PVA-CN polymer binder-bonded SnO₂ particles and (2) PVDF-bonded SnO₂ particles, respectively.

FIG. 5(A) Representative tensile stress-strain curves of three cross-linked PETEA polymers

FIG. 5(B) The discharge capacity curves of four coin cells having four different types of anode active layers: (1) high-elasticity PETEA polymer binder-bonded, carbon-coated Sn particles, (2) high-elasticity PETEA polymer binder-bonded Sn particles; (3) SBR rubber-bonded, carbon-coated Sn particles; and (d) PVDF-bonded Sn particles.

FIG. 6 Specific capacities of 2 lithium-ion cells each having Si nanowires (SiNW) as an anode active material: high-elasticity polymer binder-bonded SiNW and SBR rubber binder-bonded SiNW.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

This invention is directed at the anode active material layer (negative electrode layer, not including the anode current collector) containing a high-capacity anode material for a lithium secondary battery, which is preferably a secondary battery based on a non-aqueous electrolyte, a polymer gel electrolyte, an ionic liquid electrolyte, a quasi-solid electrolyte, or a solid-state electrolyte. The shape of a lithium secondary battery can be cylindrical, square, button-like, etc. The present invention is not limited to any battery shape or configuration or any type of electrolyte. For convenience, we will primarily use Si, Sn, and SnO₂ as illustrative examples of a high-capacity anode active material. This should not be construed as limiting the scope of the invention.

As illustrated in FIG. 1(B), a lithium-ion battery cell is typically composed of an anode current collector (e.g. Cu foil), an anode or negative electrode active material layer (i.e. anode layer typically containing particles of an anode active material, conductive additive, and binder), a porous separator and/or an electrolyte component, a cathode or positive electrode active material layer (containing a cathode active material, conductive additive, and resin binder), and a cathode current collector (e.g. Al foil). More specifically, the anode layer is composed of particles of an anode active material (e.g. graphite, Sn, SnO₂, or Si), a conductive additive (e.g. carbon black particles), and a resin binder (e.g. SBR or PVDF). This anode layer is typically 50-300 μm thick (more typically 100-200 μm) to give rise to a sufficient amount of current per unit electrode area.

In a less commonly used cell configuration, as illustrated in FIG. 1(A), the anode active material is deposited in a thin film form directly onto an anode current collector, such as a layer of Si coating deposited on a sheet of copper foil. This is not commonly used in the battery industry and, hence, will not be discussed further.

In order to obtain a higher energy density cell, the anode in FIG. 1(B) can be designed to contain higher-capacity anode active materials having a composition formula of Li_(a)A (A is a metal or semiconductor element, such as Al and Si, and “a” satisfies 0<a≤5). These materials are of great interest due to their high theoretical capacity, e.g., Li₄Si (3,829 mAh/g), Li_(4.4)Si (4,200 mAh/g), Li_(4.4)Ge (1,623 mAh/g), Li_(4.4)Sn (993 mAh/g), Li₃Cd (715 mAh/g), Li₃Sb (660 mAh/g), Li_(4.4)Pb (569 mAh/g), LiZn (410 mAh/g), and Li₃Bi (385 mAh/g). However, as discussed in the Background section, there are several problems associated with the implementation of these high-capacity anode active materials.

As schematically illustrated in FIG. 2, one major problem is the notion that, in an anode composed of these high-capacity materials, severe pulverization (fragmentation of the alloy particles) occurs during the charge and discharge cycles due to severe expansion and contraction of the anode active material particles induced by the insertion and extraction of the lithium ions in and out of these particles. The expansion and contraction of the active material particles leads to the pulverization of active material particles and detachment of the binder resin from the particles, resulting in loss of contacts between active material particles and conductive additives and loss of contacts between the anode active material and its current collector. These adverse effects result in a significantly shortened charge-discharge cycle life.

We have solved these challenging issues that have troubled battery designers and electrochemists alike for more than 30 years by developing a new class of binder resin to hold the particles of the anode active material together.

The anode active material layer comprises multiple anode active material particles and conductive additive particles that are bonded together by a high-elasticity polymer having a recoverable tensile strain no less than 5% when measured without an additive or reinforcement in the polymer under uniaxial tension and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature (preferably and more typically no less than 10⁻⁴ S/cm and more preferably and typically no less than 10⁻³ S/cm). The anode active material is preferably a high-capacity anode material that has a specific capacity of lithium storage greater than 372 mAh/g, the theoretical capacity of graphite.

High-elasticity polymer refers to a polymer, typically a lightly cross-linked polymer, which exhibits an elastic deformation that is at least 5% when measured (without an additive or reinforcement in the polymer) under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable and the recovery is essentially instantaneous upon release of the load. The elastic deformation is preferably greater than 30%, more preferably greater than 50%, further more preferably greater than 100%, still more preferably greater than 150%, and most preferably greater than 200%. The preferred types of high-capacity polymers will be discussed later.

The anode active material may be selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo₂O₄; (f) prelithiated versions thereof; (g) particles of Li, Li alloy, or surface-stabilized Li; and (h) combinations thereof. Particles of Li or Li alloy (Li alloy containing from 0.1% to 10% by weight of Zn, Ag, Au, Mg, Ni, Ti, Fe, Co, or V element), particularly surface-stabilized Li particles (e.g. wax-coated Li particles), were found to be good anode active material per se or an extra lithium source to compensate for the loss of Li ions that are otherwise supplied only from the cathode active material. The presence of these Li or Li-alloy particles encapsulated inside an elastomeric shell was found to significantly improve the cycling performance of a lithium cell.

Pre-lithiation of an anode active material can be conducted by several methods (chemical intercalation, ion implementation, and electrochemical intercalation). Among these, the electrochemical intercalation is the most effective. Lithium ions can be intercalated into non-Li elements (e.g. Si, Ge, and Sn) and compounds (e.g. SnO₂ and Co₃O₄) up to a weight percentage of 54.68% (see Table 1 below). For Zn, Mg, Ag, and Au encapsulated inside an elastomer shell, the amount of Li can reach 99% by weight.

TABLE 1 Lithium storage capacity of selected non-Li elements. Intercalated Atomic weight Atomic weight of Max. wt. % compound of Li, g/mole active material, g/mole of Li Li₄Si 6.941 28.086 49.71 Li_(4.4)Si 6.941 28.086 54.68 Li_(4.4)Ge 6.941 72.61 30.43 Li4.4Sn 6.941 118.71 20.85 Li₃Cd 6.941 112.411 14.86 Li₃Sb 6.941 121.76 13.93 Li_(4.4)Pb 6.941 207.2 13.00 LiZn 6.941 65.39 7.45 Li₃Bi 6.941 208.98 8.80

The particles of the anode active material may be in the form of a nano particle, nano wire, nano fiber, nano tube, nano sheet, nano platelet, nano disc, nano belt, nano ribbon, or nano horn. They can be non-lithiated (when incorporated into the anode active material layer) or pre-lithiated to a desired extent (up to the maximum capacity as allowed for a specific element or compound.

Preferably and typically, the high-elasticity polymer has a lithium ion conductivity no less than 10⁻⁵ S/cm, more preferably no less than 10⁻⁴ S/cm, further preferably no less than 10⁻³ S/cm, and most preferably no less than 10⁻² S/cm. In some embodiments, the high-elasticity polymer is a neat polymer having no additive or filler dispersed therein. In others, the high-elasticity polymer is a polymer matrix composite containing from 0.1% to 50% (preferably 1% to 35%) by weight of a lithium ion-conducting additive dispersed in a high-elasticity polymer matrix material. The high-elasticity polymer must have a high elasticity (elastic deformation strain value >10%). An elastic deformation is a deformation that is fully recoverable and the recovery process is essentially instantaneous (no significant time delay). The high-elasticity polymer can exhibit an elastic deformation from 5% up to 1,000% (10 times of its original length), more typically from 10% to 800%, and further more typically from 50% to 500%, and most typically and desirably from 70% to 300%. It may be noted that although a metal typically has a high ductility (i.e. can be extended to a large extent without breakage), the majority of the deformation is plastic deformation (non-recoverable) and only a small amount of elastic deformation (typically <1% and more typically <0.2%).

In some preferred embodiments, the high-elasticity polymer contains a lightly cross-linked network polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, ethylene oxide linkage, propylene oxide linkage, vinyl alcohol linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof, in the cross-linked network of polymer chains. These network or cross-linked polymers exhibit a unique combination of a high elasticity (high elastic deformation strain) and high lithium-ion conductivity.

In certain preferred embodiments, the high-elasticity polymer contains a lightly cross-linked network polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate (PETEA) chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.

Typically, a high-elasticity polymer is originally in a monomer or oligomer states that can be cured to form a cross-linked polymer that is highly elastic. Prior to curing, these polymers or oligomers are soluble in an organic solvent to form a polymer solution. Particles of an anode active material (e.g. SnO₂ nano particles and Si nano-wires) can be dispersed in this polymer solution to form a suspension (dispersion or slurry) of an active material particle-polymer (monomer or oligomer) mixture. This suspension can then be subjected to a solvent removal treatment while individual particles remain substantially separated from one another. The polymer (or monomer or oligomer) precipitates out to deposit on surfaces of these active material particles. This can be accomplished, for instance, via spray drying, ultrasonic spraying, air-assisted spraying, aerosolization, and other secondary particle formation procedures.

For instance, ethoxylated trimethylopropane triacrylate monomer (ETPTA, Mw=428, chemical formula given below), along with an initiator, can be dissolved in an organic solvent, such as ethylene carbonate (EC) or diethyl carbonate (DEC). Then, anode active material particles (Si, Sn, SnO₂, and Co₃O₄ particles, etc.) can be dispersed in the ETPTA monomer/solvent/initiator solution to form a slurry, which can be spray-dried to form ETPTA monomer/initiator-embraced anode particles. These embraced particles can then be thermally cured to obtain the particulates composed of anode particles encapsulated with a thin layer of a high-elasticity polymer. The polymerization and cross-linking reactions of this monomer can be initiated by a radical initiator derived from benzoyl peroxide (BPO) or AIBN through thermal decomposition of the initiator molecule. The ETPTA monomer has the following chemical formula:

As another example, the high-elasticity polymer for encapsulation may bes based on cationic polymerization and cross-linking of the cyanoethyl polyvinyl alcohol (PVA-CN, Formula 2) in succinonitrile (SN).

The procedure may begin with dissolving PVA-CN in succinonitrile (NCCH₂CH₂CN) to form a mixture solution. This is followed by adding an initiator into the mixture solution. For instance, LiPF₆ can be added into the PVA-CN/SN mixture solution at a weight ratio (selected from the preferred range from 20:1 to 2:1) to form a precursor solution. Then, particles of a selected anode active material are introduced into the mixture solution to form a slurry. The slurry may then be subjected to a micro-encapsulation procedure to produce anode active material particles coated with an embracing layer of reacting mass, PVA-CN/LiPF₆. These embraced particles can then be heated at a temperature (e.g. from 75 to 100° C.) for 2 to 8 hours to obtain high-elasticity polymer-encapsulated anode active material particles. During this process, cationic polymerization and cross-linking of cyano groups on the PVA-CN may be initiated by PF₅, which is derived from the thermal decomposition of LiPF₆ at such an elevated temperature.

It is essential for these materials to form a lightly cross-linked network of polymer chains that chemically bond to the active material particles. In other words, the network polymer or cross-linked polymer should have a relatively low degree of cross-linking or low cross-link density to impart a high elastic deformation.

The cross-link density of a cross-linked network of polymer chains may be defined as the inverse of the molecular weight between cross-links (Mc). The cross-link density can be determined by the equation, Mc=ρRT/Ge, where Ge is the equilibrium modulus as determined by a temperature sweep in dynamic mechanical analysis, p is the physical density, R is the universal gas constant in J/mol*K and T is absolute temperature in K. Once Ge and ρ are determined experimentally, then Mc and the cross-link density can be calculated.

The magnitude of Mc may be normalized by dividing the Mc value by the molecular weight of the characteristic repeat unit in the cross-link chain or chain linkage to obtain a number, Nc, which is the number of repeating units between two cross-link points. We have found that the elastic deformation strain correlates very well with Mc and Nc. The elasticity of a cross-linked polymer derives from a large number of repeating units (large Nc) between cross-links. The repeating units can assume a more relax conformation (e.g. random coil) when the polymer is not stressed. However, when the polymer is mechanically stressed, the linkage chain uncoils or gets stretched to provide a large deformation. A long chain linkage between cross-link points (larger Nc) enables a larger elastic deformation. Upon release of the load, the linkage chain returns to the more relaxed or coiled state. During mechanical loading of a polymer, the cross-links prevent slippage of chains that otherwise form plastic deformation (non-recoverable).

Preferably, the Nc value in a high-elasticity polymer is greater than 5, more preferably greater than 10, further more preferably greater than 100, and even more preferably greater than 200. These Nc values can be readily controlled and varied to achieve different elastic deformation values by using different cross-linking agents with different functionalities, and by designing the polymerization and cross-linking reactions to proceed at different temperatures for different periods of time.

Alternatively, Mooney-Rilvin method may be used to determine the degree of cross-linking. Crosslinking also can be measured by swelling experiments. In a swelling experiment, the crosslinked sample is placed into a good solvent for the corresponding linear polymer at a specific temperature, and either the change in mass or the change in volume is measured. The higher the degree of crosslinking, the less swelling is attainable. Based on the degree of swelling, the Flory Interaction Parameter (which relates the solvent interaction with the sample, Flory Huggins Eq.), and the density of the solvent, the theoretical degree of crosslinking can be calculated according to Flory's Network Theory. The Flory-Rehner Equation can be useful in the determination of cross-linking.

The high-elasticity polymer may contain a simultaneous interpenetrating network (SIN) polymer, wherein two cross-linking chains intertwine with each other, or a semi-interpenetrating network polymer (semi-IPN), which contains a cross-linked polymer and a linear polymer. An example of semi-IPN is an UV-curable/polymerizable trivalent/monovalent acrylate mixture, which is composed of ethoxylated trimethylolpropane triacrylate (ETPTA) and ethylene glycol methyl ether acrylate (EGMEA) oligomers. The ETPTA, bearing trivalent vinyl groups, is a photo (UV)-crosslinkable monomer, capable of forming a network of cross-linked chains. The EGMEA, bearing monovalent vinyl groups, is also UV-polymerizable, leading to a linear polymer with a high flexibility due to the presence of the oligomer ethylene oxide units. When the degree of cross-linking of ETPTA is moderate or low, the resulting ETPTA/EGMEA semi-IPN polymer provides good mechanical flexibility or elasticity and reasonable mechanical strength. The lithium-ion conductivity of this polymer is in the range of 10⁻⁴ to 5×10⁻³ S/cm.

The aforementioned high-elasticity polymers may be used alone to chemically bond the anode active material particles. Alternatively, the high-elasticity polymer can be mixed with a broad array of elastomers, electrically conducting polymers, lithium ion-conducting materials, and/or strengthening materials (e.g. carbon nanotube, carbon nano-fiber, or graphene sheets).

A broad array of elastomers can be mixed with a high-elasticity polymer to bond the anode active material particles together. The elastomeric material may be selected from natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.

The urethane-urea copolymer film usually consists of two types of domains, soft domains and hard ones. Entangled linear backbone chains consisting of poly(tetramethylene ether) glycol (PTMEG) units constitute the soft domains, while repeated methylene diphenyl diisocyanate (MDI) and ethylene diamine (EDA) units constitute the hard domains. The lithium ion-conducting additive can be incorporated in the soft domains or other more amorphous zones.

In some embodiments, a high-elasticity polymer can form a polymer matrix composite containing a lithium ion-conducting additive dispersed in the high-elasticity polymer matrix material, wherein the lithium ion-conducting additive is selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

In some embodiments, the high-elasticity polymer can be mixed with a lithium ion-conducting additive, which contains a lithium salt selected from lithium perchlorate, LiClO₄, lithium hexafluorophosphate, LiPF₆, lithium borofluoride, LiBF₄, lithium hexafluoroarsenide, LiAsF₆, lithium trifluoro-metasulfonate, LiCF₃SO₃, bis-trifluoromethyl sulfonylimide lithium, LiN(CF₃SO₂)₂, lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium nitrate, LiNO₃, Li-Fluoroalkyl-Phosphates, LiPF₃(CF₂CF₃)₃, lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

The high-elasticity polymer may form a mixture, blend, or semi-interpenetrating network with an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.

In some embodiments, the high-elasticity polymer may form a mixture or with a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), Polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVdF), Poly bis-methoxy ethoxyethoxide-phosphazenex, Polyvinyl chloride, Polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a derivative thereof (e.g. sulfonated versions), or a combination thereof.

Unsaturated rubbers that can be mixed with the high-elasticity polymer include natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR),

Some elastomers are saturated rubbers that cannot be cured by sulfur vulcanization; they are made into a rubbery or elastomeric material via different means: e.g. by having a copolymer domain that holds other linear chains together. Each of these elastomers can be used to encapsulate particles of an anode active material by one of several means: melt mixing (followed by pelletizing and ball-milling, for instance), solution mixing (dissolving the anode active material particles in an uncured polymer, monomer, or oligomer, with or without an organic solvent) followed by drying (e.g. spray drying), interfacial polymerization, or in situ polymerization of elastomer in the presence of anode active material particles.

Saturated rubbers and related elastomers in this category include EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, and protein elastin. Polyurethane and its copolymers (e.g. urea-urethane copolymer) are particularly useful elastomeric shell materials for encapsulating anode active material particles.

The binder formulation typically requires the high-elasticity polymer or its precursor (monomer or oligomer) to be dissolvable in a solvent. Fortunately, all the high-elasticity polymers or their precursors used herein are soluble in some common solvents. The un-cured polymer or its precursor can be readily dissolved in a common organic solvent to form a solution. This solution can then be used to bond solid particles via several of the binder application methods to be discussed in what follows. Upon contact with active material particles, the precursor is then polymerized and cross-linked.

The first method includes dispersing the anode active materials particles into the polymer precursor solution to form a slurry, which is then coated onto a surface of a current collector (e.g. Cu foil). The liquid medium of the coated slurry is then removed to form a dried layer containing the active material particles and conductive additive particles each partially coated with the polymer pre-cursor (monomer or oligomer). This procedure is essentially identical or very similar to the slurry coating process currently commonly used in lithium-ion battery. Hence, there is no need to change the production equipment or facility. This dried layer is exposed to heat and/or UV light to initiate the polymerization and cross-linking reactions that harden the binder resin and bonds the solid particles together. Preferably, the amount of polymer is selected in such a manner that the binder resin only covers less than 50% (preferably <20%) of the exterior surface of an active material particle.

One may also use a modified pan coating process that involves tumbling the active material particles in a pan or a similar device while the precursor solution is applied slowly until a desired amount of contact between the polymer precursor and solid active material particles is achieved. The concentration of the monomer/oligomer in the solution is selected to ensure enough polymer to help bond the active particles together, but not to cover the entire exterior surface of active material particles. Preferably, a majority of the exterior surface of an active material particle is not covered by the polymer.

Solution spraying also may be used to apply a binder resin to surfaces of active material particles supported by a solid substrate. The polymer precursor solution, along with particles of active material and conductive additive, may be spray-coated onto a surface of a current collector. Upon removal of the liquid solvent, the dried mass is subjected to thermally or UV-induced polymerization and cross-linking.

Example 1: High-Elasticity Polymer-Bonded Cobalt Oxide (Co₃O₄) Anode Particulates

An appropriate amount of inorganic salts Co(NO₃)₂.6H₂O and ammonia solution (NH₃.H₂O, 25 wt. %) were mixed together. The resulting suspension was stirred for several hours under an argon flow to ensure a complete reaction. The obtained Co(OH)₂ precursor suspension was calcined at 450° C. in air for 2 h to form particles of the layered Co₃O₄. Portion of the Co₃O₄ particles was then made into an anode active material layer using an ETPTA-based high-elasticity polymer binder according to the following procedure:

The ethoxylated trimethylopropane triacrylate monomer (ETPTA, Mw=428, Sigma-Aldrich) was dissolved in a solvent mixture of ethylene carbonate (EC)/diethyl carbonate (DEC), at a weight-based composition ratios of the ETPTA/solvent of 3/97 (w/w). Subsequently, benzoyl peroxide (BPO, 1.0 wt. % relative to the ETPTA content) was added as a radical initiator to allow for thermal crosslinking reaction after mixing with anode particles. Then, anode active material particles (Co₃O₄ particles) and some CNTs (as a conductive additive) were dispersed in the ETPTA monomer/solvent/ initiator solution to form a slurry, which was spray-coated onto a Cu foil surface to form a layer of mixture of ETPTA monomer/initiator, CNTs, and Co₃O₄ particles. This layer was then thermally cured at 60° C. for 30 min to obtain an anode active material layer composed of Co₃O₄ particles and CNTs that are bonded together by a high-elasticity polymer-based binder resin.

On a separate basis, some amount of the ETPTA monomer/solvent/initiator solution was cast onto a glass surface to form a wet film, which was thermally dried and then cured at 60° C. for 30 min to form a film of cross-linked polymer. In this experiment, the BPO/ETPTA weight ratio was varied from 0.1% to 4% to vary the degree of cross-linking in several different polymer films. Some of the cure polymer samples were subjected to dynamic mechanical testing to obtain the equilibrium dynamic modulus, Ge, for the determination of the number average molecular weight between two cross-link points (Mc) and the corresponding number of repeat units (Nc), as a means of characterizing the degree of cross-linking.

Several tensile testing specimens were cut from each cross-link film and tested with a universal testing machine. The representative tensile stress-strain curves of four BPO-initiated cross-linked ETPTA polymers are shown in FIG. 3(A), which indicate that this series of network polymers have an elastic deformation from approximately 230% to 700%. These above are for neat polymers without any additive. The addition of up to 30% by weight of a lithium salt typically reduces this elasticity down to a reversible tensile strain from 10% to 100%.

For electrochemical testing, a comparative electrode using a conventional binder resin is also prepared. The working electrodes were prepared by mixing 85 wt. % active material (Co₃O₄, particles, 7 wt. % CNTs, and 8 wt. % polyvinylidene fluoride (PVDF) binder dissolved in N-methyl-2-pyrrolidinoe (NMP) to form a slurry of 5 wt. % total solid content. After coating the slurries on Cu foil, the electrodes were dried at 120° C. in vacuum for 2 h to remove the solvent before pressing. Then, the electrodes were cut into a disk (φ=12 mm) and dried at 100° C. for 24 h in vacuum.

Electrochemical measurements were carried out using CR2032 (3V) coin-type cells with lithium metal as the counter/reference electrode, Celgard 2400 membrane as separator, and 1 M LiPF₆ electrolyte solution dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) (EC-DEC, 1:1 v/v). The cell assembly was performed in an argon-filled glove-box. The CV measurements were carried out using a CH-6 electrochemical workstation at a scanning rate of 1 mV/s.

The electrochemical performance of the cell featuring high-elasticity polymer binder and that containing PVDF binder were evaluated by galvanostatic charge/discharge cycling at a current density of 50 mA/g, using a LAND electrochemical workstation. As summarized in FIG. 3(B), the first-cycle lithium insertion capacity values are 756 mAh/g (SBR binder) and 757 mAh/g (BPO-initiated ETPTA polymer-based binder), respectively, which are higher than the theoretical values of graphite (372 mAh/g). Both cells exhibit some first-cycle irreversibility. The initial capacity loss might have resulted from the incomplete conversion reaction and partially irreversible lithium loss due to the formation of solid electrolyte interface (SET) layers.

As the number of cycles increases, the specific capacity of the SBR-bonded Co₃O₄ electrode drops precipitously. Compared with its initial capacity value of approximately 756 mAh/g, its capacity suffers a 20% loss after 175 cycles and a 27.51% loss after 260 cycles. In contrast, the presently invented high-elasticity polymer binder provides the battery cell with a significantly more stable and high specific capacity for a large number of cycles, experiencing a capacity loss of 9.51% after 260 cycles. These data have clearly demonstrated the surprising and superior performance of the presently invented high-elasticity polymer binder.

It may be noted that the number of charge-discharge cycles at which the specific capacity decays to 80% of its initial value is commonly defined as the useful cycle life of a lithium-ion battery.

The high-elasticity polymer binder appears to be capable of reversibly deforming without breakage when the anode active material particles expand and shrink. The polymer also remains chemically bonded to the anode active material particles when these particles expand or shrink. In contrast, the SBR binder is broken or detached from some of the active material particles. These were observed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.

Example 2: High-Elasticity Polymer Binder-Bonded Tin Oxide Particulates

Tin oxide (SnO₂) nano particles were obtained by the controlled hydrolysis of SnCl₄.5H₂O with NaOH using the following procedure: SnCl₄.5H₂O (0.95 g, 2.7 m-mol) and NaOH (0.212 g, 5.3 m-mol) were dissolved in 50 mL of distilled water each. The NaOH solution was added drop-wise under vigorous stirring to the tin chloride solution at a rate of 1 mL/min.

This solution was homogenized by sonication for 5 min. Subsequently, the resulting hydrosol was reacted with H₂SO₄. To this mixed solution, few drops of 0.1 M of H₂SO₄ were added to flocculate the product. The precipitated solid was collected by centrifugation, washed with water and ethanol, and dried in vacuum. The dried product was heat-treated at 400° C. for 2 h under Ar atmosphere.

The high-elasticity polymer for binding SnO₂ nano particles was based on cationic polymerization and cross-linking of the cyanoethyl polyvinyl alcohol (PVA-CN) in succinonitrile (SN). The procedure began with dissolving PVA-CN in succinonitrile to form a mixture solution. This step was followed by adding an initiator into the solution. For the purpose of incorporating some lithium species into the high elasticity polymer, we chose to use LiPF₆ as an initiator. The ratio between LiPF₆ and the PVA-CN/SN mixture solution was varied from 1/20 to ½ by weight to form a series of precursor solutions. Subsequently, particles of a selected anode active material (SnO₂ and graphene-embraced SnO₂ particles) and acetylene black particles (as a conductive additive) were introduced into these solutions to form a series of slurries. The slurries were then separately coated onto a Cu foil surface to produce an anode active material layer. The layer was then heated at a temperature from 75 to 100° C. for 2 to 8 hours to obtain a layer of high-elasticity polymer-bonded anode active material particles.

Additionally, the reacting mass, PVA-CN/LiPF₆, was cast onto a glass surface to form several films which were polymerized and cross-linked to obtain cross-linked polymers having different degrees of cross-linking. Tensile testing was also conducted on these films and some testing results are summarized in FIG. 4(A). This series of cross-linked polymers can be elastically stretched up to approximately 80% (higher degree of cross-linking) to 400% (lower degree of cross-linking).

The battery cells from the high-elasticity polymer-bonded particles (nano-scaled SnO₂ particles) and PVDF-bonded SnO₂ particles were prepared using a procedure described in Example 1. FIG. 4(B) shows that the anode prepared according to the presently invented high-elasticity polymer binder approach offers a significantly more stable and higher reversible capacity compared to the PVDF-bonded SnO₂ particle-based anode. The high-elasticity polymer is more capable of holding the anode active material particles and conductive additive together, significantly improving the structural integrity of the active material electrode.

Example 3: Tin (Sn) Nano Particles Bonded by a PETEA-Based High-Elasticity Polymer

For serving as a resin binder to bond Sn nano particles together, pentaerythritol tetraacrylate (PETEA), Formula 3, was used as a monomer:

The precursor solution was composed of 1.5wt. % PETEA (C₁₇H₂₀O₈) monomer and 0.1wt. % azodiisobutyronitrile (AIBN, C₈H₁₂N₄) initiator dissolved in a solvent mixture of 1,2-dioxolane (DOL)/dimethoxymethane (DME)(1:1 by volume). Nano particles (76 nm in diameter) of Sn were added into the precursor solution, which was coated onto a Cu foil. The PETEA/AIBN precursor solution was polymerized and cured at 70° C. for half an hour to obtain an anode layer.

The reacting mass, PETEA/AIBN (without Sn particles), was cast onto a glass surface to form several films which were polymerized and cured to obtain cross-linked polymers having different degrees of cross-linking. Tensile testing was also conducted on these films and some testing results are summarized in FIG. 5(A). This series of cross-linked polymers can be elastically stretched up to approximately 25% (higher degree of cross-linking) to 80% (lower degree of cross-linking)

For comparison, some amount of Sn nano particles was bonded by SBR binder to make an anode. Shown in FIG. 5(B) are the discharge capacity curves of four coin cells having four different types of Sn-based anode layers: (1) high-elasticity PETEA polymer binder-bonded, carbon-coated Sn particles, (2) high-elasticity PETEA polymer binder-bonded Sn particles; (3) SBR rubber-bonded, carbon-coated Sn particles; and (d) PVDF-bonded Sn particles. These results have clearly demonstrated that the high-elasticity polymer binder strategy provides excellent protection against capacity decay of a lithium-ion battery featuring a high-capacity anode active material (having either encapsulated by carbon or non-encapsulated particles). Carbon encapsulation alone is not effective in providing the necessary protection against capacity decay.

The high-elasticity polymer binder appears to be capable of reversibly deforming without breakage when the anode active material particles expand and shrink. The polymer also remains chemically bonded to the anode active material particles when these particles expand or shrink. In contrast, both SBR and PVDF, the two conventional binder resins, are broken or detached from some of the active material particles. These were observed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.

Example 4: Si Nanowire-Based Particulates Protected by a High-Elasticity Polymer

Si nano particles and Si nanowires Si nano particles are available from Angstron Energy Co. (Dayton, Ohio). Si nanowires, mixtures of Si and carbon, and their graphene sheets-embraced versions, respectively, were mixed with particles of acetylene black (a conductive additive) and formed into an active material layer using the instant polymers as a binder resin (semi-interpenetrating network polymer of ETPTA/EGMEA and the cross-linked BPO/ETPTA polymer, as in Example 1).

For bonding various anode particles together by the ETPTA semi-IPN polymer, the ETPTA (Mw=428 g/mol, trivalent acrylate monomer), EGMEA (Mw=482 g/mol, monovalent acrylate oligomer), and 2-hydroxy-2-methyl-1-phenyl-1-propanone (HMPP, a photoinitiator) were dissolved in a solvent (propylene carbonate, PC) to form a solution. The weight ratio between HMPP and the ETPTA/EGMEA mixture was varied from 0.2% to 2%. The ETPTA/EGMEA proportion in the solution was varied from 1% to 5% to generate different encapsulation layer thicknesses. The ETPTA/EGMEA ratio in the acrylate mixture was varied from 10/0 to 1/9.

Spray-coating was used to produce the electrode over a sheet of Cu foil. The active material layer containing ETPTA/EGMEA/HMPP was then exposed to UV irradiation for 20 s. The UV polymerization/cross-linking was conducted using a Hg UV lamp (100 W), having a radiation peak intensity of approximately 2000 mW/cm² on the surfaces of the electrodes.

The above procedure was conducted to produce electrode layers that were bonded by a cross-linked ETPTA/EGMEA polymer. For comparison purposes, electrodes containing Si nanowires bonded by SBR binder were also prepared and implemented in separate lithium-ion cells. The cycling behaviors of these 2 cells are shown in FIG. 6, which indicates that high-elasticity polymer binder-bonded Si nanowires provide significantly more stable cycling response.

Example 5: Effect of Lithium Ion-Conducting Additive in a High-Elasticity Polymer Shell

A wide variety of lithium ion-conducting additives were added to several different polymer matrix materials to prepare binder resin materials for maintaining structural integrity of electrodes. We have discovered that these polymer composite materials are suitable binder materials. Since the high-elasticity polymer can cover a significant portion of the active material particle surface, this polymer (with or without the lithium ion-conducting additive) must be capable of allowing lithium ions to readily diffuse through. Hence, the polymer must have a lithium ion conductivity at room temperature no less than 10⁻⁵ S/cm.

TABLE 2 Lithium ion conductivity of various high-elasticity polymer composite compositions as a shell material for protecting anode active material particles. Sample Lithium-conducting No. additive Elastomer (1-2 μm thick) Li-ion conductivity (S/cm) E-1b Li₂CO₃ + (CH₂OCO₂Li)₂ 70-99% PVA-CN 2.9 × 10⁻⁴ to 3.6 × 10⁻³ S/cm E-2b Li₂CO₃ + (CH₂OCO₂Li)₂ 65-99% ETPTA 6.4 × 10⁻⁴ to 2.3 × 10⁻³ S/cm E-3b Li₂CO₃ + (CH₂OCO₂Li)₂ 65-99% ETPTA/EGMEA 8.4 × 10⁻⁴ to 1.8 × 10⁻³ S/cm D-4b Li₂CO₃ + (CH₂OCO₂Li)₂ 70-99% PETEA 7.8 × 10⁻³ to 2.3 × 10⁻² S/cm D-5b Li₂CO₃ + (CH₂OCO₂Li)₂ 75-99% PVA-CN 8.9 × 10⁻⁴ to 5.5 × 10⁻³ S/cm B1b LiF + LiOH + Li₂C₂O₄ 60-90% PVA-CN 8.7 × 10⁻⁵ to 2.3 × 10⁻³ S/cm B2b LiF + HCOLi 80-99% PVA-CN 2.8 × 10⁻⁴ to 1.6 × 10⁻³ S/cm B3b LiOH 70-99% PETEA 4.8 × 10⁻³ to 1.2 × 10⁻² S/cm B4b Li₂CO₃ 70-99% PETEA 4.4 × 10⁻³ to 9.9 × 10⁻³ S/cm B5b Li₂C₂O₄ 70-99% PETEA 1.3 × 10⁻³ to 1.2 × 10⁻² S/cm B6b Li₂CO₃ + LiOH 70-99% PETEA 1.4 × 10⁻³ to 1.6 × 10⁻² S/cm C1b LiClO₄ 70-99% PVA-CN 4.5 × 10⁻⁴ to 2.4 × 10⁻³ S/cm C2b LiPF₆ 70-99% PVA-CN 3.4 × 10⁻⁴ to 7.2 × 10⁻³ S/cm C3b LiBF₄ 70-99% PVA-CN 1.1 × 10⁻⁴ to 1.8 × 10⁻³ S/cm C4b LiBOB + LiNO₃ 70-99% PVA-CN 2.2 × 10⁻⁴ to 4.3 × 10⁻³ S/cm S1b Sulfonated polyaniline 85-99% ETPTA 9.8 × 10⁻⁵ to 9.2 × 10⁻⁴ S/cm S2b Sulfonated SBR 85-99% ETPTA 1.2 × 10⁻⁴ to 1.0 × 10⁻³ S/cm S3b Sulfonated PVDF 80-99% ETPTA/EGMEA 3.5 × 10⁻⁴ to 2.1 × 10⁻⁴ S/cm S4b Polyethylene oxide 80-99% ETPTA/EGMEA 4.9 × 10⁻⁴ to 3.7 × 103⁴ S/cm

Example 6: Cycle Stability of Various Rechargeable Lithium Battery Cells

In lithium-ion battery industry, it is a common practice to define the cycle life of a battery as the number of charge-discharge cycles that the battery suffers 20% decay in capacity based on the initial capacity measured after the required electrochemical formation. Summarized in Table 3 below are the cycle life data of a broad array of batteries featuring presently invented electrodes containing anode active material particles bonded by different binder materials.

TABLE 3 Cycle life data of various lithium secondary (rechargeable) batteries. Initial Cycle life Sample capacity (No. of ID Binder resins Type & % of anode active material (mAh/g) cycles) Si-1b PVA-CN 25% by wt. Si nano particles (80 1,120 1,150 nm) + 67% graphite + 8% binder Si-2b SBR 25% by wt. Si nano particles (80 1,119 155 nm) + 67% graphite + 8% binder SiNW-1b SBR 45% Si nano particles, pre- 1,258 255 lithiated SiNW-2b PVA-CN + 50% 45% Si nano particles, pre-ithiated 1,760 1,250 ethylene oxide VO₂-1b ETPTA 90%-95%, VO₂ nano ribbon 255 1,140 VO₂-2b PVDF 90%-95%, VO₂ nano ribbon 720 147 SnO₂-2b ETPTA/EGMEA + 75% SnO₂ particles (3 μm initial 740 1,280 20% polyanniline size) SnO₂-2b ETPTA/EGMEA 75% SnO₂ particles (3 μm initial 738 1,626 size) Ge-1b PETEA 85% Ge + 8% graphite platelets + 850 1,552 binder Ge-2b PVDF 85% Ge + 8% graphite platelets + 856 145 binder

These data further confirm that the high-elasticity polymer binder strategy is surprisingly effective in alleviating the anode expansion/shrinkage-induced capacity decay problems. 

1.-27. (canceled)
 28. A method of manufacturing a lithium battery, said method comprising: (a) providing a cathode active material layer and an optional cathode current collector to support said cathode active material layer; (b) providing an anode active material layer and an optional anode current collector to support said anode active material layer; and (c) providing an electrolyte in contact with the anode active material layer and the cathode active material layer and an optional separator electrically separating the anode and the cathode; wherein the operation of providing the anode active material layer includes bonding multiple particles of an anode active material and an optional conductive additive together to form said layer by a binder resin containing a high-elasticity polymer having a recoverable tensile strain from 5% to 700% when measured without an additive or reinforcement and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature.
 29. A method of manufacturing a lithium battery, said method comprising: (a) providing a cathode active material layer and an optional cathode current collector to support said cathode active material layer; (b) providing an anode active material layer and an optional anode current collector to support said anode active material layer; and (c) providing an electrolyte in contact with the anode active material layer and the cathode active material layer and an optional porous separator electrically separating the anode and the cathode; wherein the operation of providing the anode active material layer includes bonding multiple particles of an anode active material and an optional conductive additive together by a binder resin to form said anode active material layer and applying a thin film of a high-elasticity polymer to cover and protect said anode active material layer, wherein said high-elasticity polymer has a recoverable or elastic tensile strain from 5% to 700% when measured without an additive or reinforcement and a lithium ion conductivity no less than 10⁻⁵ S/cm at room temperature and said thin film has a thickness from 1 nm to 10 μm.
 30. The method of claim 29, wherein said thin film of high-elasticity polymer is implemented between said anode active material layer and said porous separator.
 31. The method of claim 28, wherein said high-elasticity polymer has a lithium ion conductivity from 1×10⁻⁵ S/cm to 2×10⁻² S/cm.
 32. The method of claim 28, wherein said high-elasticity polymer has a recoverable tensile strain from 10% to 300%.
 33. The method of claim 28, wherein said high-elasticity polymer contains a cross-linked network polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, ethylene oxide linkage, propylene oxide linkage, vinyl alcohol linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof in said cross-linked network of polymer chains.
 34. The method of claim 28, wherein said high-elasticity polymer contains a cross-linked network of polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.
 35. The method of claim 28, wherein said high-elasticity polymer forms a mixture with an elastomer, an electronically conductive polymer, a lithium-ion conducting material, a reinforcement material, or a combination thereof.
 36. The method of claim 35, wherein said lithium ion-conducting material is dispersed in said high-elasticity polymer and is selected from Li₂CO₃, Li₂O, Li₂C₂O₄, LiOH, LiX, ROCO₂Li, HCOLi, ROLi, (ROCO₂Li)₂, (CH₂OCO₂Li)₂, Li₂S, Li_(x)SO_(y), or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.
 37. The method of claim 35, wherein said lithium ion-conducting material is dispersed in said high-elasticity polymer and is selected from lithium perchlorate, LiClO₄, lithium hexafluorophosphate, LiPF₆, lithium borofluoride, LiBF₄, lithium hexafluoroarsenide, LiAsF₆, lithium trifluoro-metasulfonate, LiCF₃SO₃, bis-trifluoromethyl sulfonylimide lithium, LiN(CF₃SO₂)₂, lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium oxalyldifluoroborate, LiBF₂C₂O₄, lithium nitrate, LiNO₃, Li-Fluoroalkyl-Phosphates, LiPF₃(CF₂CF₃)₃, lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.
 38. The method of claim 28, wherein said anode active material is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (c) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo₂O₄; (d) prelithiated versions thereof; (e) mixtures thereof with a carbon, graphene, or graphite material; (f) particles of Li, Li alloy, or surface-stabilized Li having at least 60% by weight of lithium element therein; and (f) combinations thereof.
 39. The method of claim 28, wherein said one or a plurality of anode active material particles is coated with a layer of carbon or graphene.
 40. The method of claim 28, wherein said one or a plurality of anode active material particles is mixed with a carbon, graphene, or graphite material to form a mixture and said mixture is embraced by one or a plurality of graphene sheets.
 41. The method of claim 29, wherein said one or plurality of anode active material particles are mixed with a carbon material, a graphite material, and/or graphene sheets to form a mixture that is embraced by external graphene sheets to form graphene-embraced anode active material particulates, which are then bonded by the binder resin. 